Electrical Joule Heating and Early Strength of Mineral-impregnated Carbon Fibre Reinforcement (MCF)

Abstract

Mineral-impregnated carbon fibre reinforcement (MCF) has attracted increasing attention due to its low-cost, easy manufacturing, high temperature and chloride resistance, when it replaces traditional steel reinforcement for concrete construction. Considering its excellent electrical conductivity, this paper investigates the effect of electrical Joule heating on the temperature increase, mechanical and microstructural characteristics of MCF. Different duration of electrical heating ranging from 0.5h, 1h, 2h, 4h to 8h had been explored. In addition, the effect of water spray treatment on the electrically heated MCF will be conducted. For the MCF reference without electrical heating, it is not hardened and the early flexural strength can’t be obtained. The temperature of MCF under the voltage of 15 V gradually increases to 100.5 °C and then keeps stable. The highest early flexural strength of MCF immediately tested after heating reached 290.8 MPa when the electrical heating time is 8h, and with the water spray treatment. Interestingly, the water spray treatment seems to benefit the strength development, with the less generated micro pores around the interfaces of carbon fibres to cement matrix. The results indicate that the rapid hardening MCF subjected to electrical heating can work as self-heating elements or rapid production and transportation of MCF for concrete structures.

Full Paper