This research aims to compare corrosion parameters obtained by linear polarization technique and Tafel extrapolation method in steel bars embedded in concrete. It was analyzing the intervention of mineral additions, such as metakaolin (10%) in binary concrete mixtures and silica fume (9% ) and nano silica (1%) in ternary concrete mixtures of water/binder ratio of 0.4 and 0.6 after induction of corrosion by wetting and drying cycles in a solution containing chlorides. Thus, the corrosion potential (Ecorr), polarization resistance (Rp) and corrosion rate (icorr) were measured. As a main result, a good correlation (R² of 0.82 and 0.96) was obtained with the values of polarization resistance (Rp) and corrosion rate (icorr), obtained by Rp and by Tafel slope, respectively. Binary and ternary concretes mixtures showed higher performance than reference concretes. Reference concrete with w/ratio of 0.6 showed a high corrosion rate. | This research aims to compare corrosion parameters obtained by linear polarization technique and Tafel extrapolation method in steel bars embedded in concrete. It was analyzing the intervention of mineral additions, such as metakaolin (10%) in binary concrete mixtures and silica fume (9% ) and nano silica (1%) in ternary concrete mixtures of water/binder ratio of 0.4 and 0.6 after induction of corrosion by wetting and drying cycles in a solution containing chlorides. Thus, the corrosion potential (Ecorr), polarization resistance (Rp) and corrosion rate (icorr) were measured. As a main result, a good correlation (R² of 0.82 and 0.96) was obtained with the values of polarization resistance (Rp) and corrosion rate (icorr), obtained by Rp and by Tafel slope, respectively. Binary and ternary concretes mixtures showed higher performance than reference concretes. Reference concrete with w/ratio of 0.6 showed a high corrosion rate. | ||
| + | |||
| + | == Full Paper == | ||
| + | <pdf>Media:Draft_Sanchez Pinedo_94602242831.pdf</pdf> | ||
Latest revision as of 10:22, 3 October 2023
Abstract
This research aims to compare corrosion parameters obtained by linear polarization technique and Tafel extrapolation method in steel bars embedded in concrete. It was analyzing the intervention of mineral additions, such as metakaolin (10%) in binary concrete mixtures and silica fume (9% ) and nano silica (1%) in ternary concrete mixtures of water/binder ratio of 0.4 and 0.6 after induction of corrosion by wetting and drying cycles in a solution containing chlorides. Thus, the corrosion potential (Ecorr), polarization resistance (Rp) and corrosion rate (icorr) were measured. As a main result, a good correlation (R² of 0.82 and 0.96) was obtained with the values of polarization resistance (Rp) and corrosion rate (icorr), obtained by Rp and by Tafel slope, respectively. Binary and ternary concretes mixtures showed higher performance than reference concretes. Reference concrete with w/ratio of 0.6 showed a high corrosion rate.
Full Paper
Document information
Published on 03/10/23
Submitted on 03/10/23
DOI: 10.23967/c.dbmc.2023.031
Licence: CC BY-NC-SA license
Share this document
Keywords
claim authorship
Are you one of the authors of this document?